Excellent Impact Resistance. Applications include automotive articles, e.g. car bumpers, battery cases,  etc.

Material Tested to Industry standards over a wide range of temperatures (See ISO Test results below).

Successful Independent Operational, and drop tests carried out on the Pro-lock device between -55degC and +55degC. No significant deterioration in strength or problems with operation noted.

Resistance to oils and greases.

UV stabilized.

Tenalle Strength at yield

Flexural Modulus

Tensile Modulus

Elongation at Yield

Izod Impact notched at 23°C

Izod Impact notched at -20°C

Charpy Impact Strength notched at 23°C

Charpy Impact Strength notched at -20°C

Hardness Rockwell - R-scale

Melting Point

Vicat Softening Temperature 10N-50°C per hr

Density

Bulk Density

MPa

MPa

MPa

%

KJ/m2

KJ/m2

KJ/m2

KJ/m2

°C

°C

g/cm2

g/cm2

ISO 527-2

ISO 176

ISO 527-2

ISO 527-2

ISO 180

ISO 180

ISO 179

ISO 179

ISO 2039-2

ISO 3146

ISO 306

ISO 1183

ISO 1183

26

1400

1500

10

9

5.5

10

5

85

165

145

.905

.525

M8 x 30mm 304/S15 Stainless Steel bolt

M8 x 16mm Torq thru insert, or M8 nut, fabricated from 303 Stainless Steel.

Specification to BS 302 1987

2.5mm Diameter, PVC Coated to 3.5mm

7 strands

Minimum breaking load of wire 435kgs

Safe Working Load 87kgs

Note: SWL applies to rope only. Pro-lock is not a lifting device.